| Q04-2各色硝基外用磁漆 |
|
| |
1、组成 |
|
| |
该漆是由硝化棉、油改性醇酸树脂、各种颜料、增韧剂和混合溶剂等研磨调制而成。
|
|
| 2、性能： |
|
漆膜干燥快、平整光亮，耐候性较好。能用砂蜡打磨抛光。
|
|
| 3、用途 |
|
主要用作难于烘烤而装饰性要求较高的大型设备和工件，如各种交通车辆、机床、机器设备和工具的保护装饰。
|
|
| 4、主要技术指标： |
|
项目 |
技术指标 |
漆膜颜色加外观 |
符合标准色板及
色差、平整光滑 |
粘度（涂-4粘度计） S |
70-200 |
干燥时间 min≤ |
|
表干 |
10 |
实干 |
|
| 光泽 %≥ |
|
浅、中色 |
70 |
深色 |
80 |
硬度 ≥ |
0.5 |
冲击强度 cm≥ |
30 |
附着力 级≤ |
2 |
|
|
| 5、使用说明 |
|
（1）、该漆涂覆在喷过底漆的无油垢表面上，与底漆结合力较好，宜选用与硝基漆配套的底漆。
（2）、使用前将漆搅拌均匀，如有机械杂质应予过滤。
（3）、施工以喷涂为主，用X-1硝基稀释剂稀释，在湿度很高的地方施工，如漆膜发现发白，可适当加入F-1硝基漆防潮剂或乙酸丁酯与丁醇
（1：1）的混合溶剂调整。
（4）、施工时，两次喷涂间隔以10min左右为宜。
（5）、铝粉漆配漆量最好按需用调配。
|
|
| 6、标志、包装、贮存和运输 |
|
按Q/320500ZQ02-90《涂料产品标志、包装、贮存和运输规则执行》。有效贮存期为一年。
|
|
| Co4-2Nitrocellulose Enamel Lacquer in Colours |
|
| 1、Composition |
|
| The paint is composed of nitrocotton,oil-modified alkyd resin,grinded pigments,toughner and organic solbent. |
|
| 2、Performance |
|
| The paint fiml is rapid drying ,smooth,glossy and polishable with sang wax ,also has good weatherability. |
|
| 3、Application |
|
The paint is especially used in huge equipments and impements with high requirement for decoration but poor bakeable,such as behicles,machinetools,
machines etc. |
| 4、Maint technical index |
Item |
Index |
1)Film
colour and appearance
|
smooth and bright in accordance with standard sample and its range of colour difference |
2)Viscosity,seconds
Ford cup No.4
|
70-200 |
|
3)Drying time,minutes
surface dry(tack free) ≤
complete dry ≤ |
10
50
|
|
4)Gloss, %
light and medium colour≥
dark colour
≥ |
70
80
|
5）Hardness ≥ |
0.5 |
6)Impact strength,cm ≥ |
|
7)Adhesion,grade ≤ |
2 |
|
| 5、Application directions |
1)Coat the paint on the oil-free surface,which the primer has been sprayed on ,will get a better adhesiveness between the two coatings.
It is important to select a proper primer which forms a complete set with Nitro-lacquer.
2)Before application,the paint should be stirred to uniform.In case of mechanical impurity,the paint should be filtrated.
3)The paint should be applied with spraying.
X-1 Nitro-diluent may be used.
At the site of high humidity,if the film blushing is found under applying,F-1 Nitro-moistrue proof agent or mixed-solvent of buty` acetate/butanol(1:1)may be added in properly.
4)Make sure 10 minutes interval between the two courses.
5)It is better to formulate the proper amount of aluminium paint as needed.
|
| 6、Mark,Package,Storage and Trancsportation |
Carry out Q/320500 ZQ02-90《The Regulations of Mark,Package,Storage and Transportation forPaint Products.》
The storage life is one year.
|
|
|